Abstract
Optical materials capable of dynamically manipulating electromagnetic waves are an emerging field in memories, optical modulators, and thermal management. Recently, their multispectral design preliminarily attracts much attention, aiming to enhance their efficiency and integration of functionalities. However, the multispectral manipulation based on these materials is challenging due to their ubiquitous wavelength dependence restricting their capacity to narrow wavelengths. In this article, we cascade multiple tunable optical cavities with selective-transparent layers, enabling a universal approach to overcoming wavelength dependence and establishing a multispectral platform with highly integrated functions. Based on it, we demonstrate the multispectral (ranging from 400 nm to 3 cm), fast response speed (0.9 s), and reversible manipulation based on a typical phase change material, vanadium dioxide. Our platform involves tandem VO2-based Fabry–Pérot (F-P) cavities enabling the customization of optical responses at target bands independently. It can achieve broadband color-changing capacity in the visible region (a shift of ~60 nm in resonant wavelength) and is capable of freely switching between three typical optical models (transmittance, reflectance, and absorptance) in the infrared to microwave regions with drastic amplitude tunability exceeding 0.7. This work represents a state-of-art advance in multispectral optics and material science, providing a critical approach for expanding the multispectral manipulation ability of optical systems.
Similar content being viewed by others
Introduction
The demand for advanced applications in fields such as memories, information communication, imaging, and medical health has spurred the development of optical systems operating across broadband wavelengths ranging from the visible (VIS), infrared (IR) to terahertz (THz) and microwave (MW) regions1,2,3. For example, the development of materials with high IR emittance and solar reflectance can motivate terrestrial surfaces to cool themselves passively by harvesting the coldness of the universe4,5,6. However, optical systems with fixed spectra may generate undesired outcomes in non-standard conditions, such as overcooling7,8 and invalid concealment9,10,11,12,13, significantly limiting their practical applications.
Optical systems produced by phase change materials (PCMs)14,15,16,17 and electrochromic materials (ECMs)18,19,20 can overcome these challenges by dynamically changing optical responses under external stimulations. Overcooling can be prevented by automatically reducing the IR emittance when the temperature drops7. However, the strong and ubiquitous wavelength dependence observed in PCMs and ECMs restricts their unique optical properties to certain wavelengths21. Moreover, structures such as metasurfaces and optical cavities, which are deliberately designed to improve the efficiency of these materials, tend to exacerbate this limitation (Supplementary Fig. S1). As a result, optical systems that exhibit reversible tunability face severe challenges in achieving multispectral manipulation (Supplementary Table S1).
A significant breakthrough occurred when Kocabas et al.21 developed a multilayer graphene (MLG) based electrochemical optical platform capable of dynamically modulating reflectivity across a broad range of the swath from the VIS to MW regions. The MLG, which possesses high electrical conductivity (<50 Ω·sq−1), was laminated and vacuum sealed in a low-density polyethylene pouch. With optical transparency exceeding 90%, it can replace the top electrode and allows for broadband optical activity, opening up a new avenue for the development of ECMs-based optical systems. However, the ionic migration occurring inside ECMs inevitably leads to a relatively long response time in the range of dozens of seconds and additional energy consumption. The permanent tunable path from high absorption to high reflectance precludes possibilities of transmittance regulation. Despite the fair optical tunability of PCMs under external stimulations, their multispectral operations remain unreported due to the unbroken wavelength dependence (Supplementary Table S1).
In this article, we propose a universal method to breaking up the wavelength dependence of a typical PCM-vanadium dioxide (VO2), and demonstrate its multispectral manipulation with reversible tunability covering wavelengths ranging from the VIS to MW regions. The VO2-based system is capable of constructing a broadband color-changing space in the VIS region, and to the best of our knowledge, could switch freely between three typical optical models (transmittance, reflectance, and absorptance) in the IR to MW regions for the first time. Moreover, the ultrafast phase transition of VO2 enables faster response time of 0.9 s compared to ECMs-based systems. The unparalleled performance is unachievable for any reported optical system and represents a significant breakthrough in multispectral optics.
Results
Operating principle and ideal spectrum
Figure 1a demonstrates the proposed tandem Fabry–Pérot (F-P) cavity structure and its fundamental operating principle. At the critical temperature of 340 K, VO2 undergoes an ultrafast transformation from monoclinic VO2(M) to rutile VO2(R), accompanied by an energy band change that leads to the transition from insulating to metallic behaviors (Fig. 1b). The phase transition leads to high contrast in its optical behaviors from VIS to MW regions, thereby endowing VO2 with the potential for multispectral manipulation22,23,24,25,26,27. In the VIS region, the top VO2/HfO2/VO2/Si F-P cavity (TFP) enables the device to change reflective colors by adjusting resonant wavelengths during the phase transition. We choose Si, rather than the widely used Al, Ag or Au layers, as the bottom reflector in TFP to block VIS waves, because the transparency of Si in the IR to MW regions ensures the optical accessibility of the bottom cavity. Interestingly, TFP can be viewed as VO2/Si bi-layer due to the disappeared wavelength-dependent F-P effect when facing IR to MW waves, and determine the state of F-P resonance in the bottom F-P cavity (BFP) by the phase transition of VO2. Therefore, BFP can be regarded as a VO2/dielectric layer/VO2 tri-layer typical F-P structure, and is able to create a moveable F-P resonance peak in IR when VO2 is metallic. The bottom VO2 in BFP can block IR to MW waves due to the excellent conductivity of metallic VO2(R) while being transparent for insulating VO2(M). This is the key strategy to achieve comprehensive optical manipulation involving transmittance and meanwhile provide adequate reflectance in IR simultaneously. Figure 1c demonstrates the ideal multispectral manipulation in the proposed system based on the measured data: (i) broadband color-changing ability in VIS; (ii) drastic transmittance tunability from zero to near unity in the IR, THz and MW regions; (iii) A dynamic absorptance region whose peak position is also adjustable in IR and longer wavelengths; (iv) ultrafast switching speed. The experimental results demonstrate that our system is the only one reported so far, achieving multispectral and dynamic manipulation with ultrafast response speed based on PCM (Fig. 1d)18,21,28,29,30,31,32,33,34,35,36.
Limitations of existing VO2-based systems in multispectral operations
The ubiquitous wavelength dependence of PCMs and ECMs confines their functionality to specific wavelengths21, whose modulation efficiency deteriorates seriously at other bands. We explore the wavelength dependence of VO2-based optical systems by the simulated thickness-dependent VIS-MIR reflectance tunability spectra of representative VO2-based platforms (VO2/SiO2, VO2/Al, and VO2/HfO2/Al). As shown in Fig. 2, it is apparent that there exists a certain region possessing the best modulation efficiency for fixed thickness. These regions shift to a longer wavelength with the increasing VO2 thickness and exhibit the typical sub-wavelength feature as a joint effect of the thickness-dependent interference effect37 and the intrinsic absorptance of VO2. Besides the strong wavelength dependence, the poor color-changing ability of VO2 in VIS and the shielding effect of common substrates (Al, Au, SiO2, et al.) in the IR to MW regions further limit the potential of VO2 for multispectral manipulation. Therefore, there are several issues in achieving the multispectral manipulation based on VO2: (i) improve the color-changing ability; (ii) overcome the wavelength dependence and (iii) break the shielding effect of substrates.
Structural design for TFP operating in the VIS region
The slight permittivity discrepancy in the VIS region during the phase transition induces an inconspicuous color change of VO238. (Supplementary Fig. S2a, b) Herein, as shown in Fig. 3a, we construct a TFP structure consisting of VO2/HfO2/VO2/Si layers to amplify the permittivity change of VO2 in the VIS region, and realize a reversible tuning of the reflective color. The top VO2 film acts as the semi-transparent layer and the bottom VO2 acts as a part of the dielectric layer. A 150-nm-thick Si layer is chosen as the substrate to block the propagation of VIS waves, while maintaining high transparency when facing IR to MW waves. (Fig. 3a and Supplementary Fig. S2c) The interactive disturbance in optical designs for TFP and BFP is simultaneously eliminated. Considering the coherent accumulation of the partial waves reflected from the F–P cavity39,40, the F-P resonant wavelength λ in TFP can be calculated as:
where nD is the effective refractive index of dielectric layers consisting of HfO2 and VO2, dD is the thickness of dielectric layers, θ is the incident angle, φ21 and φ23 represent the phase shift of the reflection coefficients at the top VO2/HfO2 interface and the VO2/Si interface. According to Eq. 1, \({n}_{D}\) is the primary factor contributing to tuning \({\rm{\lambda }}\) and changing surface colors during the phase transition. Meanwhile, different combinations of \({d}_{D}\), \({\varphi }_{21}\) and \({\varphi }_{23}\) enable the construction of a broadband color-changing gamut theoretically.
We then investigate the color-changing capacity of TFP by simulating the temperature-dependent reflectance spectra. For preset structural parameters (10 nm VO2/25 nm HfO2/40 nm VO2/150 nm Si), the amplified decrease in \({n}_{D}\) during the phase transition prompts the blue shift of the reflectance valley from 610 nm to 575 nm, with an encouraging color change observed from cyan to purple (Supplementary Fig. S2d and Fig. 3b). We further explore the potential of enriching the color-changing space by modifying structural parameters. Our calculations, presented in the CIE 1931 color space, demonstrate that it is achievable to gain diverse color-changing paths by varying the thickness of VO2 layers (Fig. 3c–f). TFP with a top-layer VO2 thinner than 20 nm exhibits superior dynamic color-changing capabilities across the phase transition. The ultra-thin thickness of each layer in TFP also ensures that it is optically accessible to BFP devices in the IR to MW regions. This section theoretically proves the capacity of TFP to generate broadband colors and determines an approximate thickness range for TFP41.
Structural design for BFP operating in the IR to MW regions
Manipulating IR waves usually changes objects’ radiative properties, and further affects their heat exchange process. Thereby, the comprehensive capacity to switch between the three states of transmission, reflection, and absorption is crucial for a thermal regulator42. Constructing F-P cavities is the most common and efficient method to enhance the capacity of dynamic manipulating absorptance for VO2 in the IR to MW regions. However, as mentioned before, the strong wavelength dependence confines the spectral width, and the dynamic manipulation of transmittance is not supported as well.
Herein, we propose a “two birds with one stone” method that replaces the metal reflector with a VO2 layer, whose reflection to IR, THz and MW waves is activated in its metallic state, and therefore achieves the broadband manipulation of transmittance while maintaining the resonant absorption in an F-P cavity (Fig. 4a). Simulated spectra in Supplementary Fig. S3 find that the minimum thickness for a VO2 layer to provide adequate reflectance in the IR region is around 300 nm. In this article, we choose a 500 nm thickness VO2 layer as the reflector for simulations and experiments.
Then we investigate the effect of structural parameters in TFP on the performance of BFP. As shown in Supplementary Fig. S4, the small deviations in spectra between the two structures reveal that it is acceptable to regard the VO2/HfO2/VO2 tri-layers in TFP as a monolayer VO2 layer whose thickness is the sum of the thickness of two VO2 layers. Supplementary Fig. S5 indicates that arbitrary thickness combinations of the two VO2 layers in TFP have no impact on the IR performance when maintaining the sum of their thickness to be a constant, but meanwhile, the system could exhibit diverse surface color appearances. It represents the achievable independent spectral manipulation in divided wavelengths. Meanwhile, we discover the effect of HfO2 thickness (varies from 0 to 2000 nm) on the IR performance of BFP and the comprehensive modulation paths covering the transmittance, reflectance and absorptance (Supplementary Fig. S6 and Fig. 4b, c). When VO2 is insulating, the system exhibits a maximum transmittance exceeding 0.7 because of the negligible optical loss in each layer. The reflectance at regions shorter than 5 μm increases slightly as a result of the refractive mismatch in interfaces within TFP, which indicates the sub-wavelength, or wavelength-dependence effect of optical systems. After the phase transition, the completely forbidden transmission in the IR region leads to a drastic transmittance tunability of 0.7. The F-P resonance generates a strong absorption peak whose position is adjustable by varying the thickness of HfO2 in BFP. In the non-resonant regions, the VO2(R) reflector enhances the reflectance significantly with maximum tunability exceeding 0.7. For potential applications requiring not only tunable amplitude but a moveable absorptance peak wavelength, it is also feasible by replacing the HfO2 layer with dielectric materials with changeable refractive index, such as liquid crystals43, GST alloys44.
In the THz and MW regions, the dielectric constants of VO2 can be described using the Drude model45,46:
where ε∞ = 12 is dielectric permittivity at the infinite frequency, \({\omega }_{p}(\sigma )\) is the plasma frequency of VO2 that dependent on conductivity,\(\gamma\) = 5.75 ×1013 rad· s−1 is the collision frequency, \({\sigma }_{0}\) = 3 ×105 S· m−1,\(\,{\omega }_{p}({\sigma }_{0})\) = 1.5 ×1015 rad· s−1, \(\sigma\) is the conductivity of VO2 (Fig. 4d and Supplementary Fig. S7). As shown in Fig. 4e, when VO2 is insulating, BFP exhibits a completely transmissive state due to the lossless layers and the disappearance of interlayer interaction due to the wavelength dependence. After the phase transition, the transmittance drastically becomes 0, where the reflectance reaches 0.8 simultaneously. The performance may contribute to the combined applications of communications, computations and electromagnetic shielding47,48. In addition, systems deposited on substrates with different optical properties can bestow more manipulation paths in the IR to MW regions. Supplementary Fig. S8 demonstrates the simulated IR to MW spectra of systems deposited on totally absorptive/reflective substrates (Fig. 4e can be regarded as the spectrum of the system deposited on a transparent substrate). The radically different features in these spectra will activate and support much more insights into expansive multispectral applications.
Experimental demonstration and characterization
To further validate the promise of multispectral dynamic manipulation, we develop proof of concept (PoC) samples. (see Methods for details) A 300 μm thickness Si wafer with high transparency in the IR, THz and MW regions is chosen as the substrate to discover the consistency between experiments and simulations. The membrane thicknesses in TFP, from top to bottom, are 15, 35, 20, and 150 nm. The samples are labeled Sample-1, Sample-2, and Sample-3, based on the different thicknesses (0, 600, and 1200 nm) of the HfO2 layer in BFP. The thickness of the bottom VO2 in BFP maintains 500 nm. (Fig. 5a and Supplementary Fig. S9) Measured physical properties of the deposited VO2 films are presented in Supplementary Fig. S10.
In the VIS region, an apparent reflective color change from purple to pink is observed in Fig. 5a and Supplementary Movie 1 when heating the samples to 100 °C. The color change path meets well with the simulation in Fig. 2e, f. The blue shift of the F-P resonance in TFP during the phase transition is also detected in the measured temperature-dependent reflectance spectra, though errors of optical constants induce some mismatch in the intensity compared to the simulated spectra (Supplementary Fig. S11). Therefore, it is achievable to generate arbitrary colors by simply altering the layer thickness in TFP, which expands the potential of VO2-based optical systems in the fields of color display and adaptive camouflage. Meanwhile, the response time can be ascertained by measuring the time interval between the sample’s contact with the heater and its full discoloration, which occurs in approximately 0.9 s (Supplementary Fig. S12).
In the IR region, a measured maximum transmittance difference of 0.6 across the phase transition of VO2 in Supplementary Fig. S13a indicates the success in introducing the reversible tunability of transmittance into a multispectral optical system. The system exhibits an anti-reflection effect on the Si substrate so that the transmittance at around 7 μm is even higher than that of the substrate. The decreased transmittance in longer wavelengths due to the increased absorption of thicker HfO2 can be addressed by replacing the HfO2 dielectric layer with an IR lossless material. A large reflectance tunability of around 0.5 is also presented in Supplementary Fig. S13b. We further investigate the adjustable absorption performance of the samples. Figure 5b shows near-perfect absorption peaks generated by the F-P resonance in BFP when VO2 is metallic in all samples, which indicates a high absorptance tunability reaching 0.7 at resonant wavelengths, and the position can be easily adjusted within a wide range (3-11 μm) even extended to the THz and MW regions49,50 (Supplementary Fig. S13c). In addition, we further verify the effect of substrates on the dynamic manipulation path in the IR region. We put three samples on substrates with high emittance (SiO2 wafer) and high reflectance (Al wafer), then record the temperature-dependent IR images and videos (Fig. 5c and Supplementary Movies 2-3). The high transparency makes samples’ IR performance depend on the substrate at low temperatures, while eventually coming to a substrate-independent high absorptance state after the VO2 phase transition. Therefore, it is achievable to construct two distinctly opposite temperature-dependent absorptance tunability paths in the IR region, which can be adapted to requirements of different IR applications (Fig. 5d).
In the THz and MW regions, a sharp change of conductivity with more than three orders of magnitude is observed for a 500 nm VO2 layer deposited on a Si substrate (Fig. 4d). Measured temperature-dependent transmittance spectra in the THz and MW regions exhibit drastic transmittance tunability exceeding 0.7 for all samples (Fig. 5e). The wavelength dependence keeps THz and MW spectra unchangeable with varying HfO2 thicknesses. The absorptance of the Si substrate triggers a slight degeneracy in transmittance when VO2 is insulating compared to simulations.
Finally, response time, as another critical performance of multispectral manipulation, is also crucial21. The ultrafast phase transition of VO2 under the picosecond scale endows this system with an incomparable response time and has been widely confirmed51. Therefore, our work reports an unparalleled performance in multispectral manipulation (Fig. 1d and Supplementary Table S1).
Discussion
In summary, we propose a universal method for overcoming the wavelength dependence of tunable optical materials, and have demonstrated the exceptional potential of modified tandem VO2-based F-P cavities for multispectral and reversible manipulation spanning from the VIS to MW regions. The multispectral platform achieves unprecedented performance, including broadband color-changing capability in the VIS region and free switching ability among three optical states of transmittance, reflectance, and absorptance in the IR to MW regions. Moreover, the ultrafast phase transition of VO2 enables a short response time of less than 0.9 s. Our work represents the state-of-the-art level in interdisciplinary research that interfaces multispectral optics and material science. We believe it will open up a wide range of possibilities for advanced applications in memories, thermal management, imaging, and communications.
Methods
Simulation method
Electromagnetic wave calculations are performed using FDTD Solutions, a commercially available FDTD simulation software from Lumerical Solutions, Canada. All of the simulations reported in this paper are performed in three-dimensional layouts. We use the periodic boundary conditions along the x and y axes, and use perfectly matched layers along the z axis. Mesh accuracy is set to 8, and the minimum mesh step is 0.00025 μm. The minimum auto shutoff is 10−5. A plane wave is chosen as the source which injects along the z axis. The transmittance and reflectance are monitored by power monitors. Optical constants of used materials at different regions can be found in the reference52. The physical optical models for VO2 at metallic and insulating states can be described as Eq. (4)53
VO2 layer deposition
VO2 layers were deposited by a high-power pulsed magnetron sputtering system (MS650C) purchased from KeYou, China. During the deposition process, the Ar/O2 ratio was fixed at 81:1.9 sccm, and the sputtering power was set to 180 W. The chamber pressure, substrate temperature, input pulse frequency and width were fixed at 0.9 Pa, 550 °C, 200 Hz and 50 μs, respectively.
HfO2 layer deposition
HfO2 layers were deposited by a direct current magnetron sputtering system (MS650C) purchased from KeYou, China. During the deposition process, the Ar/O2 ratios were fixed at 81:6.8 sccm, and the sputtering powers were set to 220 W. The chamber pressure and the substrate temperature were fixed at 0.9 Pa, 400 °C, respectively.
Si layer deposition
The Si layer was deposited by a radio frequency magnetron sputtering system (MS650C) purchased from KeYou, China. During the deposition process, the Ar/O2 ratios were fixed at 81:0 sccm, and the sputtering powers were set to 100 W. The chamber pressure and the substrate temperature were fixed at 0.9 Pa, 100 °C, respectively.
Measurements
The crystalline phases were characterized using X-ray diffraction (XRD, PANalytical B.V. Model Xpert Pro). The Raman spectrum was recorded by an inVia Laser Micro Raman spectrometer (Renishaw, UK) equipped with a confocal microscope and a 532 nm excitation laser source. The cross-sectional images were evaluated by a field emission transmission electron microscope (JEOL JEM-F200). TEM samples were prepared by a focused ion beam (FIB) instrument (Hitachi NX5000). Fourier transform infrared (FT-IR) spectroscopy was performed using an FT-IR system (VERTEX-70, Bruker) from 2.5 to 25 μm. X-ray photoelectron spectroscopy (XPS) was performed with a PHI 5700 ESCA System using Al Ka radiation (1486.6 eV). XPS data were calibrated to the C1s peak and analyzed using Casa XPS software. The IR images were recorded by thermal imager (TIX-660, FLUKE) from 7.5 to 14 μm. The conductivity was measured by Hall Effect Measurement System (Ecopia HMS-3000).
References
Li, Y. et al. Transforming heat transfer with thermal metamaterials and devices. Nat. Rev. Mater. 6, 488–507 (2021).
Liu, T. J. et al. Thermal photonics with broken symmetries. eLight 2, 25 (2022).
Huang, G. et al. Upconversion nanoparticles for super-resolution quantification of single small extracellular vesicles. eLight 2, 20 (2022).
Yin, X. B. et al. Terrestrial radiative cooling: Using the cold universe as a renewable and sustainable energy source. Science 370, 786–791 (2020).
Li, T. et al. A radiative cooling structural material. Science 364, 760–763 (2019).
Zeng, S. N. et al. Hierarchical-morphology metafabric for scalable passive daytime radiative cooling. Science 373, 692–696 (2021).
Tang, K. C. et al. Temperature-adaptive radiative coating for all-season household thermal regulation. Science 374, 1504–1509 (2021).
Wang, S. C. et al. Thermochromic smart windows with highly regulated radiative cooling and solar transmission. Nano Energy 89, 106440 (2021).
Hu, R. et al. Thermal camouflaging metamaterials. Mater. Today 45, 120 (2021).
Tang, K. C. et al. A thermal radiation modulation platform by emissivity engineering with graded metal–insulator transition. Adv. Mater. 32, 1907071 (2020).
Qin, B. et al. Whole-infrared-band camouflage with dual-band radiative heat dissipation. Light Sci. Appl. 12, 246 (2023).
Xu, Z. Q. et al. Spatially resolved dynamically reconfigurable multilevel control of thermal emission. Laser Photonics Rev. 14, 1900162 (2020).
Hou, J. F. & Situ, G. Image encryption using spatial nonlinear optics. eLight 2, 3 (2022).
Abdollahramezani, S. et al. Electrically driven reprogrammable phase-change metasurface reaching 80% efficiency. Nat. Commun. 13, 1696 (2022).
Wei, H. et al. Smart materials for dynamic thermal radiation regulation. Small 17, 2100446 (2021).
Dou, S. L. et al. Bioinspired microstructured materials for optical and thermal regulation. Adv. Mater. 33, 2000697 (2021).
Shahsafi, A. et al. Temperature-independent thermal radiation. Proc. Natl Acad. Sci. USA 116, 26402–26406 (2019).
Li, M. Y. et al. Manipulating metals for adaptive thermal camouflage. Sci. Adv. 6, eaba3494 (2020).
Ergoktas, M. S. et al. Graphene-enabled adaptive infrared textiles. Nano Lett. 20, 5346–5352 (2020).
Strand, M. T. et al. Polymer inhibitors enable >900 cm2 dynamic windows based on reversible metal electrodeposition with high solar modulation. Nat. Energy 6, 546–554 (2021).
Ergoktas, M. S. et al. Multispectral graphene-based electro-optical surfaces with reversible tunability from visible to microwave wavelengths. Nat. Photonics 15, 493–498 (2021).
Cui, Y. Y. et al. Thermochromic VO2 for energy-efficient smart windows. Joule 2, 1707–1746 (2018).
Shi, R. et al. Recent advances in fabrication strategies, phase transition modulation, and advanced applications of vanadium dioxide. Appl. Phys. Rev. 6, 011312 (2019).
Lai, W. E. et al. Fully optically tunable and flexible composite films for enhanced terahertz control and multifunctional terahertz devices. ACS Appl. Electron. Mater. 3, 3044–3051 (2021).
Shi, R. et al. Liquid precursor-guided phase engineering of single-crystal VO2 beams. Angew. Chem. Int. Ed. 62, e202301421 (2023).
Shi, R. et al. Phase management in single-crystalline vanadium dioxide beams. Nat. Commun. 12, 4214 (2021).
Chen, B. W. et al. Directional terahertz holography with thermally active Janus metasurface. Light Sci. Appl. 12, 136 (2023).
Shao, Z. W. et al. All-solid-state proton-based tandem structures for fast-switching electrochromic devices. Nat. Electron. 5, 45–52 (2022).
Yuan, L. M. et al. A dynamic thermal camouflage metadevice with microwave scattering reduction. Adv. Sci. 9, 2201054 (2022).
Li, W. J. et al. Effect of independently controllable electrolyte ion content on the performance of all-solid-state electrochromic devices. Chem. Eng. J. 398, 125628 (2020).
Mandal, J. et al. Li4Ti5O12: a visible-to-infrared broadband electrochromic material for optical and thermal management. Adv. Funct. Mater. 28, 1802180 (2018).
Zhang, X. et al. Preparation and performances of all-solid-state variable infrared emittance devices based on amorphous and crystalline WO3 electrochromic thin films. Sol. Energy Mater. Sol. Cells 200, 109916 (2019).
Zhao, Y. M. et al. Preparation of Sn-NiO films and all-solid-state devices with enhanced electrochromic properties by magnetron sputtering method. Electrochim. Acta 367, 137457 (2021).
Wang, S. C. et al. Scalable thermochromic smart windows with passive radiative cooling regulation. Science 374, 1501–1504 (2021).
Zhang, X. et al. Three-dimensional electrochromic soft photonic crystals based on MXene-integrated blue phase liquid crystals for bioinspired visible and infrared camouflage. Angew. Chem. Int. Ed. 61, e202211030 (2022).
Hao, Q. et al. VO2/TiN plasmonic thermochromic smart coatings for room-temperature applications. Adv. Mater. 30, 1705421 (2018).
Gu, J. X. et al. Fabrication and performances of double-sided HfO2 anti-reflection films with ultra-high infrared transmittance. J. Alloy. Compd. 858, 158337 (2021).
Boyce, A. M. et al. Actively tunable metasurfaces via plasmonic nanogap cavities with sub-10-nm VO2 films. Nano Lett. 22, 3525–3531 (2022).
Zhao, J. C. et al. Defining deep-subwavelength-resolution, wide-color-gamut, and large-viewing-angle flexible subtractive colors with an ultrathin asymmetric fabry–perot lossy cavity. Adv. Optical Mater. 7, 1900646 (2019).
Zhao, J. C. et al. Flexible dynamic structural color based on an ultrathin asymmetric Fabry-Perot cavity with phase-change material for temperature perception. Opt. Express 29, 23273–23281 (2021).
Fröch, J. E. et al. Real time full-color imaging in a Meta-optical fiber endoscope. eLight 3, 13 (2023).
Peng, Y. C. & Cui, Y. Advanced textiles for personal thermal management and energy. Joule 4, 724–742 (2020).
Li, W. L. et al. Dual-color terahertz spatial light modulator for single-pixel imaging. Light Sci. Appl. 11, 191 (2022).
Tittl, A. et al. A switchable mid-infrared plasmonic perfect absorber with multispectral thermal imaging capability. Adv. Mater. 27, 4597–4603 (2015).
Song, Z. Y., Chen, A. P. & Zhang, J. H. Terahertz switching between broadband absorption and narrowband absorption. Opt. Express 28, 2037–2044 (2020).
Zeng, D. W. et al. Dynamically electrical/thermal-tunable perfect absorber for a high-performance terahertz modulation. Opt. Express 30, 39736–39746 (2022).
Chen, Z. G. & Segev, M. Highlighting photonics: looking into the next decade. eLight 1, 2 (2021).
Ni, Y. B. et al. Computational spectropolarimetry with a tunable liquid crystal metasurface. eLight 2, 23 (2022).
Zhu, H. Z. et al. Multispectral camouflage for infrared, visible, lasers and microwave with radiative cooling. Nat. Commun. 12, 1805 (2021).
Chen, H. H. et al. Graphene-based materials toward microwave and terahertz absorbing stealth technologies. Adv. Optical Mater. 7, 1801318 (2019).
Xu, C. H. et al. Transient dynamics of the phase transition in VO2 revealed by mega-electron-volt ultrafast electron diffraction. Nat. Commun. 14, 1265 (2023).
Gu, J. X. et al. VO2-based infrared radiation regulator with excellent dynamic thermal management performance. ACS Appl. Mater. Interface 14, 2683–2690 (2022).
Kana, J. B. K. et al. Thermally tunable optical constants of vanadium dioxide thin films measured by spectroscopic ellipsometry. Opt. Commun. 284, 807–812 (2011).
Acknowledgements
We thank the National Key R&D Program of China (2022YFB3902704), the Fundamental Research Funds for the Central Universities (Grant No. HIT.DZJJ.2023038), the Science Foundation of National Key Laboratory of Science and Technology on Advanced Composites (JCKYS2023603C009), the National Natural Science Foundation of China (52272291). the China Scholarship Council (202206120085).
Author information
Authors and Affiliations
Contributions
H.W. conceived the idea, performed the simulations, and wrote the manuscript. J.G. and T.Z. fabricated the devices and measured the performance. Z.Y. and H.-X.X. revised the manuscript. H.W., S.D., C.-W.Q. and Y.L. supervised the project.
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare no competing interests.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wei, H., Gu, J., Zhao, T. et al. Tunable VO2 cavity enables multispectral manipulation from visible to microwave frequencies. Light Sci Appl 13, 54 (2024). https://doi.org/10.1038/s41377-024-01400-w